现在的办公室装修中,玻璃隔断的使用率大大增加,而对于办公室玻璃隔断装修中,一项重要的问题是双层玻璃隔断中的结露结霜现象,那么该如何防止办公室玻璃隔断结露结霜的问题。
In the present office decoration, the use rate of glass partition is greatly increased, and an important problem for the glass partition decoration in the office is the condensation and frosting in the double glazing, so how to prevent the frost of the office glass from frosting.
玻璃隔断的露点是指密封于空气层中的空气湿度达到饱和状态时的温度。低于该温度,空气层中的水蒸汽就会凝结成液态水。因此可能会出现一种情况,就是水的含量越高,空气的露点温度也就越高,当玻璃内表面温度低于空气层内空气的露点时,空气中的水分就会在玻璃内表面结露或结霜。
The dew point of glass partition refers to the temperature at which the air humidity in the air layer is saturated. Below this temperature, the water vapor in the air layer will be condensed into liquid water. Therefore, there may be a situation where the higher the water content, the higher the dew point temperature of the air, and when the inner surface temperature of the glass is lower than the dew point in the air, the moisture in the air will be exposed or frosted on the inner surface of the glass.

济南玻璃隔断

双层玻璃隔断的露点上升是由外界的水分进入空气层而不被干燥剂吸收而造成的,有以下几种原因可能会导致露点上升:密封胶内存有气泡,导致空气水分进入;水气通过聚合物扩散进入空气层中;办公室玻璃隔断的干燥剂有效吸附能力低。

The rise of the double glazed dew point is caused by the outside water entering the air layer and not absorbed by the drier. There are several reasons that may cause the dew point to rise: the sealant has bubbles in the memory, causing the air to enter the air; the water vapor enters the air layer through the polymer; the desiccant of the office glass partition is available. The efficiency of adsorption is low.
办公室双层玻璃隔断露点的控制措施:
Control measures for office double glazing partition dew point:
1.严格控制办公室双层玻璃隔断生产环境温度的变化,生产环境主要影响附能力及剩余吸附能力。
1. strictly control the temperature change in the production environment of double glazing office, and the production environment mainly affects the ability of attaching and remaining adsorption.
2.减少水分通过聚合物的扩散:主要靠选择低渗透系数的密封胶,确定合理的密封厚度,减少双层玻璃隔断的内外温度差(即控制在一定温度范围内生产而不能使温度范围过大)。
2. reduce the diffusion of water through the polymer: mainly by selecting the sealant with low permeability coefficient to determine the reasonable sealing thickness and reduce the internal and external temperature difference between the double glazing (that is, to control the production in a certain temperature range and not to make the temperature range too large).
3.缩减玻璃隔断的生产工艺时间:尽量减少干燥剂与大气接触的时间,减少吸附能力的损失而使干燥剂有较高的吸附能力。
3. reduce the production process time of glass partition: reduce the time of the contact between the desiccant and the atmosphere, reduce the loss of adsorption capacity and make the desiccant have a higher adsorption capacity.
4.选择合适的办公室玻璃隔断五金装饰:其细孔的导气缝要小,减少操作过程中分子筛的吸水率。
4. choose the right office glass partition hardware decoration: its small hole air gap should be small, reduce the water absorption rate of molecular sieve during operation.
5.选择合适玻璃隔断的干燥剂:要选择吸附率较高且持久的干燥剂。
5. choose suitable desiccant for glass partition: choose a desiccant with higher adsorption rate.